AC vs. DC Electrophoretic Deposition of Hydroxyapatite on Titanium    [PDF]

V. Ozhukil Kollatha, Q. Chen, R. Closset, J. Luyten, K. Traina, S. Mullens, A. R. Boccaccini, R. Cloots
The bio-inertness of titanium and its alloys attracts their use as bone implants. However a bioactive coating is usually necessary for improving the bone bonding of such implants. In this study, electrophoretic deposition(EPD) of hydroxyapatite (HA) powder on titanium plate was performed using butanol as solvent under direct current (DC) and alternating current (AC) fields. The zeta potential of the suspensions was measured to understand their stability and the charge on the particles. Coating thickness was varied by adjusting the voltage and time of deposition. Surface morphology and cross section thickness were studied using scanning electron microscopy and image analysis software. Surface crack density was calculated from the micrographs. The results showed that the samples of similar thickness have higher grain density when coated using AC as compared to DC EPD. This facile but novel test proves the capability of AC-EPD to attain denser and uniform HA coatings from non-aqueous medium.
View original: http://arxiv.org/abs/1306.0743

No comments:

Post a Comment