Yong Lu, Yu Yang, Fawei Zheng, Bao-Tian Wang, Ping Zhang
By performing density functional theory (DFT) +$U$ calculations, we systematically study the electronic, mechanical, tensile, and thermodynamic properties of AmO$_{2}$. The experimentally observed antiferromagnetic insulating feature [J. Chem. Phys. 63, 3174 (1975)] is successfully reproduced. It is found that the chemical bonding character in AmO$_{2}$ is similar to that in PuO$_{2}$, with smaller charge transfer and stronger covalent interactions between americium and oxygen atoms. The valence band maximum and conduction band minimum are contributed by 2$p-5f$ hybridized and 5$f$ electronic states respectively. The elastic constants and various moduli are calculated, which show that AmO$_{2}$ is less stable against shear forces than PuO$_{2}$. The stress-strain relationship of AmO$_{2}$ is examined along the three low-index directions by employing the first-principles computational tensile test method. It is found that similar to PuO$_{2}$, the [100] and [111] directions are the strongest and weakest tensile directions, respectively, but the theoretical tensile strengths of AmO$_{2}$ are smaller than those of PuO$_{2}$. The phonon dispersion curves of AmO$_{2}$ are calculated and the heat capacities as well as lattice expansion curve are subsequently determined. The lattice thermal conductance of AmO$_{2}$ is further evaluated and compared with attainable experiments. Our present work integrally reveals various physical properties of AmO$_{2}$ and can be referenced for technological applications of AmO$_{2}$ based materials.
View original:
http://arxiv.org/abs/1211.0378
No comments:
Post a Comment