Hongguo Zhang, Wenghong Wang, Enke Liu, Xiaodan Tang, Guijiang Li, Hongwei Zhang, Guangheng Wu
The magnetic compensation and magnetostriction properties in Fe doped CoCr2O4 samples have been investigated. Structural and magnetic measurements imply that the doped Fe3+ ions initially occupy the B1(Cr) sites when x<0.1, and then mainly take the A(Co) sites. This behaviour results in a role conversion of magnetic contributors and a composition compensation between two competitively magnetic sublattices at x=0.1. Temperature dependence compensation has also been found in the samples with x=0.1~0.22, with the compensation temperature in the range of 40~104 K. The Fe3+ doping also modulates the exchange interaction of the system and prevents the formation of long range conical order of spins. The magnetoelectric transition temperature at 23K in CoCr2O4 is shifted to lower temperature by increasing the dopants. The magnetostriction effect in this system has been observed for the first time. The strain has a maximum value of about 280ppm at x=0.4. The magnetostriction is in consistent with the behaviour of the two magnetic compensations.
View original:
http://arxiv.org/abs/1211.0368
No comments:
Post a Comment