T. Durga Rao, T. Karthik, Adiraj Srinivas, Saket Asthana
The polycrystalline Bi1-xHoxFeO3 (x=0, 0.05, 0.1) compounds were synthesized by conventional solid-state route. Rietveld refinement reveals that all the compounds were stabilized in rhombohedral structure with R3c (IUCr No. 161) space group. A competing ferro and anti-ferro magnetic interaction was observed in Ho-substituted compounds. A change in the Fe-O-Fe bond-angle and Fe-O bond distance increase the Neel Transition temperature with increasing Ho concentration. The appearance of peak in imaginary part of impedance (Z") for each concentration and shifting of this peak with temperature towards higher frequency side indicated that the presence of electric relaxations. Correlated Barrier Hopping model (CBH) was employed to explain the frequency and temperature dependence of ac conductivity and the mechanism of transport in the material BFO and Ho substituted BFO. Density of states near Fermi level was calculated by using the ac conductivity data.
View original:
http://arxiv.org/abs/1203.4083
No comments:
Post a Comment