Albrecht Köhler, Ivan Knez, Daniel Ebke, Claudia Felser, Stuart S. P. Parkin
In this work we are investigating the effect of strain in ultrathin Mn-Ga thin films on the magnetic properties at room temperature. Two different Mn-Ga compositions of which one is furthermore doped with Co were grown on Cr buffered MgO (001) substrates. Films with a thickness below 12nm are highly strained and it was observed that the ratio c/a vs. thickness is depending on composition. Using c/a as an order parameter the PMA is shown to be drastically reduced with increasing strain. These findings should be considered when generalizing and downscaling results obtained from films >20nm. Furthermore it has been shown, that the strain can be reduced by introducing an additional Pt buffer and thus maintaining a high PMA for a thickness as low as 6nm.