The constitutive behavior of aluminum alloy A356 in the as-cast condition has been characterized using compression tests performed over a wide range of deformation temperatures (30-500{\deg}C) and strain rates (\approx0.1-10 /s). This work is intended to support the development of process models for a wide range of conditions including those relevant to casting, forging and machining. The flow stress behavior as a function of temperature and strain rate has been fit to a modified Johnson-Cook and extended Ludwik-Hollomon expression. The data has also been assessed with both the strain-independent Kocks-Mecking and Zener-Hollomon frameworks. The predicted plastic flow stress for each expression are compared. The results indicate that the extended Ludwik-Hollomon is best suited to describe small strain conditions (stage III hardening), while the Kocks-Mecking is best employed for large strain (stage IV). At elevated temperatures, it was found that the Zener-Hollomon model provides the best prediction of flow stress.
View original:
http://arxiv.org/abs/1206.2344
No comments:
Post a Comment