Transmission electron microscopy (TEM) study on morphological changes in gold nanostructures deposited on Si (100) upon annealing under different vacuum conditions has been reported. Au thin films of thickness ~2.0 nm were deposited under high vacuum condition (with the native oxide at the interface of Au and Si) using thermal evaporation. In-situ, high temperature (from room temperature (RT) to 850\degreeC) real time TEM measurements showed the evaluation of gold nanoparticles into rectangular/square shaped gold silicide structures. This has been attributed to selective thermal decomposition of native oxide layer. Ex-situ annealing in low vacuum (10-2 mbar) at 850\degreeC showed no growth of nano-gold silicide structures. Under low vacuum annealing conditions, the creation of oxide could be dominating compared to the decomposition of oxide layers resulting in the formation of barrier layer between Au and Si.