Jiaqian Qin, Norimasa Nishiyama, Hiroaki Ohfuji, Toru Shinmei, Li Lei, Duanwei He, Tetsuo Irifune
The Vickers hardness of polycrystalline {\gamma}-B was measured using a diamond indentation method. The elastic properties of polycrystalline {\gamma}-B (B=213.9 GPa, G=227.2 GPa, and E=503.3 GPa) were determined using ultrasonic measurement at ambient condition. Under the loading force up to 20 N, our test gave an average Vickers hardness in the asymptotic-hardness region of 30.3 GPa. The average fracture toughness was measured as 4.1MPa m1/2. Additionally, We also measured the hardness and elastic properties of polycrystalline {\beta}-B and PcBN for comparison. The hardness and elastic properties for polycrystalline {\gamma}-B was found to be very close to that of PcBN. Our results suggest that the polycrystalline {\gamma}-B could be a superhard polycrystalline material for industrial applications.