L. Kilanski, R. Szymczak, W. Dobrowolski, K. Szałowski, V. E. Slynko, E. I. Slynko
We investigated the nature of the magnetic phase transition in the Ge/1-x-y/Sn/x/Mn/y/Te mixed crystals with chemical composition changing in the range of 0.083 < x < 0.142 and 0.012 < y < 0.119. The DC magnetization measurements performed in the magnetic field up to 90 kOe and temperature range 2-200 K showed that the magnetic ordering at temperatures below T = 50 K exhibits features characteristic for both spin-glass and ferromagnetic phases. The modified Sherrington - Southern model was applied to explain the observed transition temperatures. The calculations showed that the spin-glass state is preferred in the range of the experimental carrier concentrations and Mn content. The value of the Mn hole exchange integral was estimated to be J/pd/ = 0.45+/-0.05 eV. The experimental magnetization vs temperature curves were reproduced satisfactory using the non-interacting spin-wave theory with the exchange constant J/pd/ values consistent with those calculated using modified Sherrington - Southern model. The magnetization vs magnetic field curves showed nonsaturating behavior at magnetic fields B < 90 kOe indicating the presence of strong magnetic frustration in the system. The experimental results were reproduced theoretically with good accuracy using the molecular field approximation-based model of a disordered ferromagnet with long-range RKKY interaction.
View original:
http://arxiv.org/abs/1005.0922
No comments:
Post a Comment